PCP-CL102-IC

PCP-CL102-IC

 
Product Description
 
PCP-CL102-IC is a single part screen printable carbon paste for general electronic application use where a printed resistive structure is required. The paste is cured at low temperature with a resulting sheet resistance of 100 Ω/ □  /mil.
 
Product Benefits

• Good printability

• Low temperature curing

• Good screen residence time

• Compatibility with low temperature substrates such as PET and paper

Paste Preparation
 
The paste is a single part system. Gently stir before use. Avoid rapid stirring to prevent air entrapment during the stirring process. Once the paste has been removed from the container for printing, this may introduce contamination. Please do not replace the paste in the original container.
 
Properties of the Uncured Paste
 

Test	Properties
Viscosity (Pa.S)  (Lamy, Cone & plate, 50s-1, 25oC)	2.5 - 5.0
Thinner	This should normally not be required.

 
Paste Processing Conditions
 

Parameter	Typical Properties
Substrate	PET, Glass, FR4
Screen	13 µm emulsion, 325 DPI, SS
Flood Speed	50 mm/s
Print Speed	50 mm/s
Squeegee hardness	80A Durometer Shore
Squeegee pressure	5 kg
Squeegee angle	45˚
Cured thickness	15 – 20 µm
Print gap	0.2 mm
Number of stroke	2

Print structures should be processed at 140ºC in a convection oven for 30-60 mins